# YBaCuO: cubic # a=b=3.8186, c=11.6777; 90 deg # # Format parameters: Crystallographica format # column_j 4 multiplicity 'j' # column_d 5 d-spacing 'd' in [Angs] # column_F2 7 norm of scattering factor |F|^2 in [barn] # # h k l Mult. d-space 2Theta F-squared 0 0 1 2 11.6777 7.57041 76.2348 0 0 -1 2 11.6777 7.57041 76.2348 0 0 2 2 5.83885 15.1741 397.027 0 0 -2 2 5.83885 15.1741 397.027 0 0 3 2 3.89257 22.8458 2084.26 0 0 -3 2 3.89257 22.8458 2084.26 0 1 0 2 3.8843 22.895 2310.15 0 -1 0 2 3.8843 22.895 2310.15 1 0 0 2 3.8186 23.2944 1590.25 -1 0 0 2 3.8186 23.2944 1590.25 0 1 -1 4 3.68575 24.1465 79.9977 0 -1 1 4 3.68575 24.1465 79.9977 0 1 1 4 3.68575 24.1465 79.9976 0 -1 -1 4 3.68575 24.1465 79.9976 1 0 1 4 3.62948 24.5266 21.5105 1 0 -1 4 3.62948 24.5266 21.5105 -1 0 1 4 3.62948 24.5266 21.5105 -1 0 -1 4 3.62948 24.5266 21.5105 0 1 2 4 3.23404 27.5814 891.25 0 -1 -2 4 3.23404 27.5814 891.25 0 1 -2 4 3.23404 27.5814 891.25 0 -1 2 4 3.23404 27.5814 891.25 1 0 -2 4 3.19583 27.9179 1402.22 -1 0 2 4 3.19583 27.9179 1402.22 1 0 2 4 3.19583 27.9179 1402.22 -1 0 -2 4 3.19583 27.9179 1402.22 0 1 3 4 2.74953 32.566 20895.5 0 -1 -3 4 2.74953 32.566 20895.5 0 1 -3 4 2.74953 32.566 20895.5 0 -1 3 4 2.74953 32.566 20895.5 1 0 3 4 2.72593 32.8559 22705.3 1 0 -3 4 2.72593 32.8559 22705.3 -1 0 3 4 2.72593 32.8559 22705.3 -1 0 -3 4 2.72593 32.8559 22705.3 1 1 0 4 2.72309 32.8911 22369.7 1 -1 0 4 2.72309 32.8911 22369.7 -1 1 0 4 2.72309 32.8911 22369.7 -1 -1 0 4 2.72309 32.8911 22369.7 1 -1 -1 8 2.65194 33.7997 265.48 -1 1 1 8 2.65194 33.7997 265.48 1 1 1 8 2.65194 33.7997 265.48 1 1 -1 8 2.65194 33.7997 265.48 -1 -1 1 8 2.65194 33.7997 265.48 -1 -1 -1 8 2.65194 33.7997 265.48 1 -1 1 8 2.65194 33.7997 265.479 -1 1 -1 8 2.65194 33.7997 265.479 1 1 2 8 2.46789 36.4053 613.872 1 1 -2 8 2.46789 36.4053 613.872 1 -1 -2 8 2.46789 36.4053 613.872 -1 1 2 8 2.46789 36.4053 613.872 -1 -1 2 8 2.46789 36.4053 613.872 -1 -1 -2 8 2.46789 36.4053 613.872 1 -1 2 8 2.46789 36.4053 613.871 -1 1 -2 8 2.46789 36.4053 613.871 1 1 3 8 2.2313 40.4248 4476.12 -1 -1 -3 8 2.2313 40.4248 4476.12 1 1 -3 8 2.2313 40.4248 4476.11 1 -1 3 8 2.2313 40.4248 4476.11 1 -1 -3 8 2.2313 40.4248 4476.11 -1 1 3 8 2.2313 40.4248 4476.11 -1 1 -3 8 2.2313 40.4248 4476.11 -1 -1 3 8 2.2313 40.4248 4476.11